Surface Tension, Hansen Solubility Parameters, Molar Volume, Enthalpy of Evaporation, and Molecular Weight of Selected Liquids

			Polar/Dispersion				Acid-Base						Hansen Parameters
Name(1)	CAS #(2)		γS(3)	γSd(4)	γSP(5)		γS(6)	γSLW(7)	γSAB(8)	γS+ (9)	γS- (10)		δ(11)	δD(12)	δP(13)	δH(14)	Ro(15)
Polyvinyl formal	63450-15-7		-	-	-		-	-	-	-	-		-	-	-	-	-
Polyvinyl butyral	63148-65-2		-	-	-		-	-	-	-	-		24.6	19.1	9.5	12.2	10.0
														0.92(3)	4.50(3)	1.65(3)	1.53(3)
Polyetherimide (PEI)	61128-46-9		-	-	-		-	-	-	-	-		19.8	17.7	6.0	6.4	4.8
														1.07(5)	1.14(5)	2.43(5)	1.70(5)
Nylon 6,6	32131-17-2		44.8	36.3	9.8		40.2	36.9	3.3	1.5	12.1		25.8	17.2	9.9	16.5	4.4
			3.07(8)	5.63(9)	4.03(8)		3.61(2)	0.71(2)	2.90(2)	2.11(2)	13.5(2)			1.11	1.10	6.80	1.24
Nafion	31175-20-9		-	-	-		-	-	-	-	-		-	-	-	-	-
Polyetheretherketone (PEEK)	29658-26-2		42.1	36.2	5.9		-	-	-	-	-		-	-	-	-	-
			-(1)	-(1)	-(1)
Phenoxy resin	26402-79-9		-	-	-		-	-	-	-	-		-	-	-	-	-
Aramid (Kevlar)	26125-61-1		-	-	-		-	-	-	-	-		-	-	-	-	-
Polyphenylene sulfide (PPS)	26125-40-6		46.8	44.0	2.8		-	-	-	-	-		19.8	18.7	5.3	3.7	6.7
			3.29(3)	3.50(3)	0.71(3)									-(1)	-(1)	-(1)	-(1)
Polylauryl methacrylate	25719-52-2		-	-	-		-	-	-	-	-		-	-	-	-	-
Poly 2-ethylhexyl methacrylate	25719-51-1		-	-	-		-	-	-	-	-		-	-	-	-	-
Nylon 2 (polyglycine)	25718-94-9		50.1	27.9	22.2		-	-	-	-	-		-	-	-	-	-
			-(1)	-(1)	-(1)
Polystearyl methacrylate	25639-21-8		-	-	-		-	-	-	-	-		-	-	-	-	-
Nylon 11	25587-80-8		-	-	-		-	-	-	-	-		20.5	17.0	4.4	10.6	5.1
														-(1)	-(1)	-(1)	-(1)
Polypropylene glycol (PPG, polypropylene oxide)	25322-69-4		31.7	31.3	0.4		-	-	-	-	-		-	-	-	-	-
			-(1)	-(1)	-(1)
Polyethylene oxide (PEO, PEG, polyethylene glycol)	25322-68-3		42.8	30.8	12.1		45.1	44.3	0.8	0.02	58.0		-	-	-	-	-
			0.07(2)	0.21(2)	0.14(2)		1.59(4)	1.34(4)	1.60(4)	0.03(4)	10.2(4)
Polyvinyl alcohol (PVOH)	25213-24-5		-	-	-		42.0	42.0	0.0	0.0	37.0		25.2	14.7	14.1	14.9	10.5
							-(1)	-(1)	-(1)	-(1)	-(1)			2.51(4)	2.13(4)	2.18(4)	1.38(4)
Poly(L-alanine)	25191-17-7		45.2	36.0	9.2		-	-	-	-	-		-	-	-	-	-
			-(1)	-(1)	-(1)
Polytetrahydrofuran (PTHF)	25190-06-1		31.9	27.2	4.7		-	-	-	-	-		-	-	-	-	-
			0.00(2)	0.28(2)	0.28(2)
Polyethersulfone (PES)	25154-01-2		47.0	40.0	7.0		-	-	-	-	-		21.0	18.3	8.2	6.4	6.3
			-(1)	-(1)	-(1)									0.91(6)	3.10(6)	2.33(6)	2.61(6)
Polysulfone (PSU)	25135-51-7		46.6	30.4	16.2		-	-	-	-	-		21.5	18.5	8.5	7.0	9.4
			-(1)	-(1)	-(1)									2.17(3)	2.61(3)	1.12(3)	1.69(3)
Polyphenylene oxide (PPO)	25134-01-4		46.0	36.0	10.0		-	-	-	-	-		20.1	17.9	3.1	8.5	8.6
			-(1)	-(1)	-(1)									-(1)	-(1)	-(1)	-(1)
Polyvinyl ethyl ether (polyethoxyethylene)	25104-37-4		-	-	-		-	-	-	-	-		-	-	-	-	-
Polymethyl acrylate (PMA)	25087-26-7		41.4	35.6	5.8		-	-	-	-	-		-	-	-	-	-
			0.85(4)	4.12(4)	4.45(4)
Poly(hexyl methacrylate)	25087-17-6		30.0	27.6	2.5		-	-	-	-	-		-	-	-	-	-
			0.00(2)	0.78(2)	0.78(2)
Polybenzyl methacrylate	25085-83-0		-	-	-		-	-	-	-	-		-	-	-	-	-
Polymethacrylonitrile (PMAN)	25067-61-2		-	-	-		-	-	-	-	-		23.7	17.2	14.4	7.6	3.8
														-(1)	-(1)	-(1)	-(1)
Fluorinated ethylene polypropylene (FEP)	25067-11-2		19.9	17.1	2.8		17.9	17.9	0.0	0.0	0.0		19.6	19.0	4.0	3.0	4.0
			2.90(3)	2.66(3)	2.51(3)		-(1)	-(1)	-(1)	-(1)	-(1)			-(1)	-(1)	-(1)	-(1)
Polyimide (PI)	25038-81-7		47.0	38.2	8.8		44.0	42.5	1.5	0.1	6.0		-	-	-	-	-
			8.49(2)	16.8(2)	8.27(2)		-(1)	-(1)	-(1)	-(1)	-(1)
Polyethylene terephthalate (PET)	25038-59-9		43.7	36.6	7.2		45.3	42.6	1.8	0.3	3.7		20.8	18.7	6.3	6.7	6.5
			3.42(16)	4.64(16)	3.42(16)		0.78(2)	2.83(2)	0.71(2)	0.21(2)	1.06(2)			1.25(8)	2.03(8)	2.80(8)	3.36(8)
Nylon 6 (polycaprolactum, aramid 6)	25038-54-4		42.7	33.1	9.6		45.3	42.5	2.8	0.2	9.6		20.3	17.0	3.4	10.6	5.1
			6.08(2)	2.69(2)	3.39(2)		-(1)	-(1)	-(1)	-(1)	-(1)			-(1)	-(1)	-(1)	-(1)
Ethylene-propylene-diene-monomer (EPDM)	25038-36-2		35.5	29.7	5.8		-	-	-	-	-		-	-	-	-	-
		-(1)	-(1)	-(1)
Polyvinyl proprionate	25035-84-1	34.0	26.5	7.5	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyacrylonitrile (PAN)	25014-41-9	-	-	-	-	-	-	-	-	27.4	21.7	14.1	9.1	10.9
											-(1)	-(1)	-(1)	-(1)
Poly a-methyl styrene	25014-31-7	-	-	-	-	-	-	-	-	-	-	-	-	-
Polyvinyl fluoride (PVF)	24981-14-4	38.6	34.0	4.6	37.5	35.6	1.9	2.8	6.0	-	-	-	-	-
		2.85(5)	5.72(5)	4.38(5)	1.30(3)	2.08(3)	0.85(3)	4.73(3)	6.62(3)
Polytrifluoroethylene	24980-67-4	27.5	22.0	5.4	25.4	23.1	2.3	1.8	0.7	-	-	-	-	-
		3.65(3)	2.10(3)	3.20(3)	-(1)	-(1)	-(1)	-(1)	-(1)
Polyoxymethylene (POM, polyacetal, polymethylene oxide)	24969-26-4	39.0	26.2	12.8	-	-	-	-	-	-	-	-	-	-
		7.99(2)	6.15(2)	1.84(2)
Nylon 4	24938-56-5	48.5	27.8	20.7	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyvinylidene fluoride (PVDF)	24937-79-9	34.4	25.7	8.7	30.5	28.6	1.9	10.5	0.08	23.2	17.0	12.1	10.2	4.1
		4.17(4)	4.64(4)	4.81(4)	-(1)	-(1)	-(1)	-(1)	-(1)		-(1)	-(1)	-(1)	-(1)
Nylon 12	24937-16-4	38.2	33.1	5.2	41.3	37.0	4.3	0.6	7.6	22.2	18.5	8.1	9.1	6.3
		3.46(2)	3.96(2)	0.42(2)	-(1)	-(1)	-(1)	-(1)	-(1)		-(1)	-(1)	-(1)	-(1)
Nylon 6,12	24936-74-1	67.0	62.0	4.7	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Poly(2-hydroxyethyl methacrylate)	24249-16-5	-	-	-	-	-	-	-	-	-	-	-	-	-
Cellulose triacetate	9012-09-3	-	-	-	-	-	-	-	-	-	-	-	-	-
Polymethyl methacrylate (PMMA, acrylic, plexiglas)	9011-14-7	43.5	35.9	7.8	42.2	41.6	0.6	0.0	11.1	21.3	17.9	10.1	5.4	11.0
		2.88(14)	4.09(13)	3.79(13)	2.97(11)	2.36(11)	0.89(11)	0.04(11)	5.84(11)		1.37(5)	4.46(5)	3.73(5)	4.63(5)
Nylon 6,10	9008-66-6	-	-	-	-	-	-	-	-	-	-	-	-	-
Cellophane	9005-81-6	45.4	29.8	15.6	-	-	-	-	-	28.5	16.1	18.5	14.5	7.3
		-(1)	-(1)	-(1)							-(1)	-(1)	-(1)	-(1)
Polymethylphenylsiloxane	9005-12-3	-	-	-	-	-	-	-	-	-	-	-	-	-
Nitrocellulose (cellulose nitrate)	9004-70-0	-	-	-	45.1	44.8	0.3	0.01	13.3	23.5	16.2	14.1	9.5	10.7
					0.14(2)	0.21(2)	0.35(2)	0.01(2)	3.75(2)		1.06(2)	0.85(2)	1.06(2)	1.13(2)
Ethyl cellulose	9004-57-3	-	-	-	28.6	27.4	1.2	0.04	8.6	20.4	19.0	5.6	4.9	7.9
					-(1)	-(1)	-(1)	-(1)	-(1)		1.56(2)	1.84(2)	1.41(2)	2.83(2)
Cellulose acetate butyrate (CAB)	9004-36-8	-	-	-	-	-	-	-	-	22.2	17.2	13.8	2.8	12.6
										-(1)	-(1)	-(1)	-(1)
Cellulose acetate (CA)	9004-35-7	42.0	31.0	11.1	43.5	39.0	4.5	0.3	22.2	23.5	17.1	13.1	9.4	10.6
		5.44(2)	1.84(2)	3.61(2)	6.42(4)	4.20(4)	3.25(4)	0.33(4)	2.71(4)		1.58(4)	4.41(4)	3.81(4)	2.96(4)
Poly 2-ethylhexyl acrylate	9003-77-4	30.1	28.9	1.3	-	-	-	-	-	-	-	-	-	-
		0.90(3)	1.57(3)	0.78(3)
Acrylonitrile butadiene styrene (ABS)	9003-56-9	43.6	35.8	8.0	38.6	39.4	-0.8	0.9	3.7	19.2	17.0	5.7	6.8	9.4
		4.83(5)	2.77(5)	2.55(5)	4.81(2)	0.00(2)	4.88(2)	0.14(2)	2.76(2)		0.92(2)	4.17(2)	0.49(2)	2.19(2)
Polystyrene (PS)	9003-53-6	41.7	37.0	5.0	36.9	37.9	-0.9	0.1	2.2	23.9	22.8	5.8	4.3	12.7
		1.24(8)	3.47(9)	2.84(8)	5.80(3)	4.32(3)	1.68(3)	0.20(3)	2.72(3)		-(1)	-(1)	-(1)	-(1)
Polyethyl methacrylate (PEMA)	9003-42-3	35.9	26.9	9.0	-	-	-	-	-	20.0	17.5	8.5	4.7	9.6
		-(1)	-(1)	-(1)							1.34(3)	0.62(3)	3.82(3)	1.99(3)
Polyvinyl pyrrolidone (PVP)	9003-39-8	-	-	-	46.0	43.4	2.6	0.2	22.5	-	-	-	-	-
					3.61(2)	0.00(2)	3.61(2)	0.28(2)	10.2(2)
Polyethyl acrylate (PEA)	9003-32-1	37.0	30.6	6.4	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyisoprene (PIP)	9003-31-0	-	-	-	-	-	-	-	-	18.4	18.1	2.4	2.3	10.3
											2.32(3)	1.40(3)	2.66(3)	3.40(3)
Polyisobutylene (PIB, butyl (rubber)	9003-27-4	33.6	33.6	0.0	25.0	25.0	0.0	0.0	0.0	17.1	16.4	1.7	4.7	7.9
		-(1)	-(1)	-(1)	-(1)	-(1)	-(1)	-(1)	-(1)		1.26(6)	2.15(6)	2.08(6)	2.46(6)
Polyvinyl acetate (PVA)	9003-20-7	37.7	24.8	13.0	44.5	42.6	1.9	0.04	22.3	25.7	20.9	11.3	9.7	13.7
		2.89(5)	1.65(5)	1.53(5)	-(1)	-(1)	-(1)	-(1)	-(1)		-(1)	-(1)	-(1)	-(1)
Polyacrylamide	9003-05-8	52.3	26.5	25.8	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyethylene (PE)	9002-88-4	34.2	32.8	1.4	31.7	31.5	0.2	0.1	0.9	17.6	16.8	3.8	3.8	6.6
		2.45(19)	2.89(19)	1.73(19)	2.86(10)	2.93(10)	0.27(10)	0.19(10)	1.39(10)		0.88(7)	1.94(7)	2.52(7)	2.84(7)
Polyvinyl chloride (PVC)	9002-86-2	40.1	37.4	2.8	39.8	38.7	1.0	0.1	3.1	20.0	16.8	8.9	6.1	8.5
		3.80(9)	3.93(10)	2.36(9)	4.76(6)	4.33(6)	0.96(6)	0.15(6)	2.31(6)		1.65(5)	1.95(5)	1.78(5)	3.94(5)
Polyvinylidene chloride (PVDC, Saran)	9002-85-1	45.3	40.4	4.9	40.3	40.4	-0.1	0.0	2.6	23.1	19.0	9.6	9.0	5.8
		0.38(4)	2.93(4)	2.91(4)	-(1)	-(1)	-(1)	-(1)	-(1)		1.98(2)	0.64(2)	1.70(2)	2.62(2)
Polytetrafluoroethylene (PTFE)	9002-84-0	22.2	21.3	0.9	20.8	19.9	0.9	0.1	1.6	16.7	16.2	1.8	3.4	3.9
		2.54(9)	2.71(10)	0.96(9)	0.99(2)	0.35(2)	1.34(2)	0.20(2)	2.26(2)		-(1)	-(1)	-(1)	-(1)
Paraffin	8002-74-2	28.1	28.1	0.0	-	-	-	-	-	-	-	-	-	-
		3.71(7)	3.71(7)	0.00(7)
Aluminum foil (b)	7429-90-5	41.2	31.7	9.5	-	-	-	-	-	-	-	-	-	-
		2.47(2)	0.57(2)	1.91(2)
Poly n-propyl methacrylate	2210-79-9	-	-	-	-	-	-	-	-	-	-	-	-	-
2-Hydroxyethyl methacrylate (HEMA, ethylene glycol monoacrylate)	867-77-9	56.8	36.3	20.5	-	-	-	-	-	-	-	-	-	-
		1.20(2)	0.49(2)	0.71(2)
Polydiethylsiloxane (PDES)	63148-61-8	25.7	23.8	1.9	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Hexatriacontane	630-06-8	23.7	23.6	0.1	-	-	-	-	-	-	-	-	-	-
		6.71(3)	6.78(3)	0.12(3)
Polybutylene terephthalate (PBT)	26062-94-2	46.0	42.0	4.1	47.1	45.8	1.3	0.8	0.6	-	-	-	-	-
		0.24(4)	2.83(4)	2.92(4)	-(1)	-(1)	-(1)	-(1)	-(1)
Poly n-butyl methacrylate (PnBMA)	95608-33-7	32.3	27.3	5.0	-	-	-	-	-	18.4	16.0	6.2	6.6	9.5
		1.56(5)	2.59(5)	1.78(5)							-(1)	-(1)	-(1)	-(1)
Poly t-butyl methacrylate (PtBMA)	25189-00-9	30.5	26.5	4.0	-	-	-	-	-	-	-	-	-	-
		0.00(2)	0.42(2)	0.42(2)
Polyepichlorohydrin	24969-06-0	-	-	-	-	-	-	-	-	-	-	-	-	-
Polycarbonate (PC)	24936-68-3	43.4	38.2	5.2	-	-	-	-	-	22.2	19.6	8.8	5.7	10.2
		8.21(3)	9.24(3)	3.69(3)							1.75(3)	2.58(3)	1.04(3)	4.06(3)
Eicosane	112-95-8	-	-	-	-	-	-	-	-	-	-	-	-	-
Ethyl methacrylate (EMA)	97-63-2	42.0	38.8	3.2	-	-	-	-	-	-	-	-	-	-
		1.06(2)	0.42(2)	0.64(2)
Polybutadiene	9003-17-2	-	-	-	-	-	-	-	-	18.0	17.5	2.3	3.4	6.6
											-(1)	-(1)	-(1)	-(1)
Polydimethylsiloxane (PDMS)	9016-00-6	205	19.2	1.3	-	-	-	-	-	-	-	-	-	-
		1.16(6)	1.48(6)	0.66(6)
Poly iso-butyl methacrylate (PIBMA)	9011-15-8	30.9	26.3	4.7	-	-	-	-	-	20.0	18.3	4.9	6.3	9.4
		0.00(2)	0.49(2)	0.49(2)						2.11(3)	0.93(3)	5.12(3)	2.10(3)
Polychloroprene	9010-98-4	43.6	38.8	4.8	-	-	-	-	-	-	-	-	-	-
		0.00(2)	0.14(2)	0.14(2)
Poly n-butyl acrylate	9003-49-0	32.2	28.6	3.6	-	-	-	-	-	-	-	-	-
		2.12(2)	2.55(2)	0.42(2)
Polychlorotrifluoroethylene	9002-83-9	29.5	22.6	6.9	-	-	-	-	-	16.5	15.6	2.5	4.7	5.8
		1.78(3)	1.19(3)	2.89(3)							2.10(3)	1.46(3)	2.44(3)	1.56(3)
Thermoplastic polyolefin (TPO)	-	30.9	28.5	2.3	-	-	-	-	-	-	-	-	-	-
		3.45(11)	2.80(11)	3.63(11)
Polyxylylene (parylene)	-	46.3	45.7	0.6	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyvinyl octanoate	-	28.7	26.5	2.2	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyvinyl hexanoate	-	28.9	25.1	3.8	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyvinyl hexadecanoate	-	30.9	29.8	1.1	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyvinyl dodecanoate	-	29.1	27.8	1.3	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyvinyl decanoate	-	28.9	27.1	1.8	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyvinyl butyrate	-	31.1	25.8	5.3	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyurethanes	-	39.3	30.8	8.6	30.0	30.9	-0.9	0.02	10.0	22.8	18.8	10.0	8.2	9.8
		2.60(8)	3.63(8)	3.95(8)	-(1)	-(1)	-(1)	-(1)	-(1)		1.53(11)	2.54(11)	3.09(11)	3.48(11)
Polytetramethylene oxide	-	31.9	27.4	4.5	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polypropylene isophthalate	-	49.3	35.1	14.2	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polypropylene (PP)	(a)	30.1	27.7	2.4	32.0	31.7	0.3	0.2	0.4	18.0	17.7	2.9	1.2	6.2
		2.42(11)	2.46(11)	2.45(11)	3.99(8)	3.56(8)	0.76(8)	0.45(8)	0.76(8)		0.46(2)	2.80(2)	1.71(2)	1.76(2)
Poly(phosphazene)	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Polyphenyl methacrylate	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Polyoctyl methacrylate	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Poly(nonafluoroisobutyl acrylate)	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Polymethylphenylsilylene	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Poly(4-methyl pentene-1)	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Poly(hexafluoropropylene)	-	14.9	13.6	1.3	-	-	-	-	-	-	-	-	-	-
		2.10(3)	1.48(3)	1.55(3)
Poly(hexachlorobutadiene)	-	41.5	40.7	0.8	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Poly(heptafluoroisopropyl methacrylate)	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Poly(heptafluoroisopropyl acrylate)	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Poly(heptadecafluorooctyl methacrylate)	-	15.3	13.9	1.4	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)
Polyacetylene (polyethyne)	-	51.5	48.2	3.4	-	-	-	-	-	-	-	-	-	-
		0.71(2)	1.77(2)	1.06(2)
Nylon 10,10	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Nylon 9,9	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Nylon 8,8	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Nylon 7,7	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Epoxies	-	45.0	37.2	7.8	-	-	-	-	-	24.1	19.2	10.9	9.6	11.1
		4.63(5)	4.68(5)	7.00(5)							2.53(13)	2.37(13)	2.66(13)	3.98(13)
Amorphous fluoropolymer (Teflon AF)	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Poly(dimethylaminoethylmethacrylate)	-	-	-	-	-	-	-	-	-	-	-	-	-	-
Polybutylene isophthalate	-	47.8	34.9	12.9	-	-	-	-	-	-	-	-	-	-
		-(1)	-(1)	-(1)

(a) Atactic PP CAS #9003-08-0; isotactic PP CAS #25085-53-4

(b) Aluminum foil, while obviously not a polymer, is included due to its widespread use in package converting and other industries.

⁽¹⁾ Names which are most widely used to describe the material or family of materials (e.g., polyurethanes and epoxies) at hand are preferred here. Commonly used acronyms and synonyms are also shown.

⁽²⁾ CAS (Chemical Abstract Series) numbers are shown where available. In a number of instances, more than one CAS number is assigned to a given polymer — in some cases the details and nuances of these divergences are not at all clear. We have tried to reference the CAS number which appears to have the widest use with reference to the solid state properties of the given polymer.

⁽³⁾ γ_s: Total surface free energy in mJ/m² (equivalent to dynes/cm), as reported in polar/dispersion analyses.

⁽⁴⁾ γ_s^d: Dispersion component of surface free energy in mJ/m² (equivalent to dynes/cm), as reported in polar/dispersion analyses.

⁽⁵⁾ γ_s^p: Polar component of surface free energy in mJ/m² (equivalent to dynes/cm), as reported in polar/dispersion analyses.

⁽⁶⁾ γ_s: Total surface free energy in mJ/m² (equivalent to dynes/cm), as reported in acid—base analyses.

⁽⁷⁾ γ_s^LW: Lipschitz—van der Waals (non-polar) component of surface free energy in mJ/m² (equivalent to dynes/cm), as reported in acid—base analyses.

⁽⁸⁾ γ_s^AB: Lewis acid—base interaction component of surface free energy in mJ/m² (equivalent to dynes/cm), as reported in acid—base analyses.

⁽⁹⁾ γ_s^-: Base polarity (electron-donor) component of surface free energy in mJ/m² (equivalent to dynes/cm), as reported in acid—base analyses.

⁽¹⁰⁾ γ_s⁺: Acid polarity (electron-acceptor) component of surface free energy in mJ/m² (equivalent to dynes/cm), as reported in acid—base analyses.

⁽¹¹⁾ δ: Total Hansen solubility parameter (square root of the sum of squares of the average values for dispersion, polar, and hydrogen bonding components), in MPa^1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)^1/2) @ 20-25^oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.

⁽¹²⁾ δ_D: Hansen dispersion solubility parameter, in MPa^1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)^1/2) @ 20-25^oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.

⁽¹³⁾ δ_P: Hansen polar solubility parameter, in MPa^1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)^1/2) @ 20-25^oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.

⁽¹⁴⁾ δ_H: Hansen hydrogen bonding solubility parameter, in MPa^1/2 (equivalent to joules/cubic centimeter; 2.0455 x (cal/cc)^1/2) @ 20-25^oC (293.15-298.15 K). All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.

⁽¹⁵⁾ R_o: Interaction radius. All data from Hansen Solubility Parameters: A User's Handbook, 2nd Ed., C.M. Hansen, CRC Press, Boca Raton, FL, 2007.